ASTM A335 P11 is the part of ASTM A335, the pipe shall be suitable for bending, flanging, and similar forming operations, and for fusion welding.
The steel should meet the requirements of chemical composition, tensile properties and hardness. Water pressure test should be carried out in every pipe. In addition, each pipe should be inspected according to the required practice by NDT.
Mechanical test requirements for different pipelines, such as lateral or longitudinal tensile tests, flattening tests and hardness or bending tests, are presented.
The ends of each box will indicate order number, heat number, size, weight and binding or as required.
-
Outer Dimensions: 19.05mm – 114.3mm
-
Wall Thickness: 2.0mm – 14 mm
-
Length: max 16000mm
Steel grade: ASTM A335 P11
Packing:
Bare packing/bundle packing/crate packing/wooden protection at the both sides of tubes and suitably protected for sea-worthly delivery or as requested.
Inspection and Test:
Chemical Composition Inspection, Mechanical Properties Test(Tensile Strength,Yield Strength, Elongation, Flaring, Flattening, Bending, Hardness, Impact Test), Surface and Dimension Test,No-destructive Test, Hydrostatic Test.
Surface treatment:
Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting.
Both ends of each crate will indicate the order no., heat no., dimensions, weight and bundles or as requested.
ASTM A335 P11 Chemical Compositions(%)
|
Compositions
|
Data
|
|
UNS Designa-tion
|
K11597
|
|
Carbon
|
0.05-0.60
|
|
Manganese
|
0.30-0.60
|
|
Phosphorus(max.)
|
0.025
|
|
Sulfur(max.)
|
0.025
|
|
Silicon
|
0.50-1.00
|
|
Nickel
|
…
|
|
Chromium
|
1.00-1.50
|
|
Molybdenum
|
0.44-0.65
|
|
Other Elements
|
…
|
Mechanical properties for ASTM A335 P11
|
Properties
|
Data
|
|
Tensile strength, min, (MPa)
|
415 Mpa
|
|
Yield strength, min, (MPa)
|
205 Mpa
|
|
Elongation, min, (%), L/T
|
30/20
|
Material & Manufacture
Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.
Heat Treatment
Mechanical Tests Specified
-
Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
-
For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
-
For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
Notes for Hardness Test:
-
P11 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].
Notes for Bend Test:
-
For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
-
Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
-
The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.