Cr5Mo alloy tube Average carbon content: 0.15%, chromium content: 4.00～6.00%, molybdenum content: 0.45～0.60%.
Cr5Mo alloy tube heat treatment-annealing
Cr5Mo alloy pipe mechanical properties (not less than):
Cr5Mo alloy tube tensile strength (σ^b)——390MPa
Cr5Mo alloy pipe yield point (σ^s)——185MPa
Cr5Mo alloy pipe elongation rate (δ^5)——22%
Cr5Mo alloy tube high temperature strength (σ^D, 10^5h)-27MPa at 600℃
Cr5Mo alloy pipe use examples-≤600℃ high temperature furnace pipe and steel pipe parts. Cr5Mo alloy tube Average carbon content: 0.15%, chromium content: 4.00～6.00%, molybdenum content: 0.45～0.60%.