Chemical Composition, Mechanical Properties, Visual and Dimension Test, NDT, Grain Size Test
Surface treatment:
Oil-dip, Varnish, Shot Blasting
Grade and Chemical Composition (%)
Grade
C
Mn
P≤
S≤
Si
Cr
Mo
1010
0.08-0.13
0.30-0.60
0.04
0.05
-
-
-
1020
0.18-0.23
0.30-0.60
0.04
0.05
-
-
-
1045
0.43-0.50
0.60-0.90
0.04
0.05
-
-
-
4130
0.28-0.33
0.40-0.60
0.04
0.05
0.15-0.35
0.80-1.10
0.15-0.25
4140
0.38-0.43
0.75-1.00
0.04
0.05
0.15-0.35
0.80-1.10
0.15-0.25
Typical Mechanical Properties
Grade
Condition
Tensile strength
Yield stength
Elongation
Mpa(min)
Mpa(min)
%(min)
1020
CW
414
483
5
SR
345
448
10
A
193
331
30
N
234
379
22
1025
CW
448
517
5
SR
379
483
8
A
207
365
25
N
248
379
22
4130
SR
586
724
10
A
379
517
30
N
414
621
20
4140
SR
689
855
10
A
414
552
25
N
621
855
20
Rango de tamaño
Los tubos tubulares para tubos mecánicos sin costura se suministran tanto en caliente como en caliente en una amplia gama de tamaños, desde 1.375 "hasta 7.750" OD y desde 0.188 "hasta 1.625" de espesor de pared.
Cantidades mínimas
Carbono y aleación de acabado en caliente: 10,000 libras o 4,536 kilogramos mínimo.
Carbono y aleación estirados en frío: mínimo de 5,000 libras o mínimo de 125 pies, mínimo de 2,268 kilogramos o mínimo de 38,1 metros, el que sea mayor.
Variación de la cantidad: estándar ± 10% del peso ordenado, o ± 25 pies o 7.61 metros, el que sea mayor.
Configuraciones especiales
Las configuraciones de tubos sin costura especiales de Tubular Products comienzan con aceros de la más alta calidad. Se consideran cuidadosamente el grado, el análisis químico y las condiciones de la superficie, y los procesos de producción se adaptan para lograr la mejor tubería para el uso final.
Las configuraciones están formadas por un tubo redondo por estiraje en frío. El tubo se dibuja sobre un mandril con forma o a través de un molde en forma, o ambos. Se obtienen tolerancias, acabados y propiedades mecánicas mejoradas.